Epoxy Acrylate > Products > Epoxy Acrylate
 
 


GRADE FEATURES APPLICATIONS SPECIFICATIONS ETC.
viscosity
(mPa.s)
color
(Gardner)
density
(g/㎤)
molecular
weight
func. polymer solid (%) acid value
(mgKOH/g)
monomer (%)
SE 120 bisphenol A epoxy diacrylate
- light color
- high gloss
- good chemical & water resistances
- fast curing
- good hardness
- substrates : paper, wood, plastic
- lithographic and screen inks
- fast cure coatings
- overprint varnishes
- wood sealer
- laminating adhesives
3,000
at 60℃
2 max. 1.19 525 2 100 4 max. TDS
MSDS
SE 140 low viscosity modified bisphenol A epoxy diacrylate
- light color
- fast curing
- good hardness
- high gloss
- good solvent resistances
- low odor and low irritancy
- substrates : paper, wood, plastic, cardboard, chipboard
- screen ink and varnishes
- overprint varnishes
- coatings especially low odor is required
25,000
at 25℃
2 max. 1.14 500 2 70 2 max. GPTA
30
TDS
MSDS
SE 145 modified bisphenol A epoxy diacrylate with TPGDA
- light color
- good pigment wetting
- good solvent/water resistances
- high gloss
- fast curing
- good hardness
- substrates : paper, wood, plastic
- coatings for paper, wood and chipboard
- overprint varnishes
- wood sealer / top coat
- paper upgrading
25,000
at 25℃
3 max. 1.15 500 2 75 2 max. TPGDA
25
TDS
MSDS
SE 146 bisphenol A epoxy diacrylate with TPGDA
- light color
- fast curing
- good hardness
- high gloss
- good chemical resistances
- low odor
- low viscosity
- substrates : paper, wood, plastic
- lithographic and screen inks and coatings
- fast cure coatings
- overprint varnishes
- wood fillers & top coats
- laminating adhesives
11,000
at 25℃
2 max. 1.15 500 2 75 2 max. TPGDA
25
TDS
MSDS
SE 147 bisphenol A epoxy diacrylate with HDDA
- light color
- fast curing
- high gloss
- excellent water/chemical resistances
- low odor
- good hardness
- low viscosity
- substrates : paper, wood, plastic, cardboard, chipboard
- lithographic and screen inks and coatings
- fast cure coatings
- overprint varnishes
- wood fillers
- laminating adhesives
8,500
at 25℃
2 max. 1.15 500 2 80 2 max. HDDA
20
TDS
MSDS
SE 148 bisphenol A epoxy diacrylate with TMPTA
- light color
- high gloss
- good chemical resistances
- fast curing
- good hardness
- low odor
- substrates : paper, wood, plastic, cardboard, chipboard
- lithographic and screen inks and coatings
- fast cure coatings
- overprint varnishes
- wood fillers
- paper upgrading
55,000
at 25℃
2 max. 1.17 500 2 80 2 max. TMPTA
20
TDS
MSDS
SE 1500 low viscosity version of SE 1701
- excellent flexibility & toughness
- good abrasion resistance
- excellent solvent resistance
- good adhesion
- low viscosity & easy handling
- high gloss
- substrates : paper, wood, chip board, plastics
- lithographic and screen inks
- clear coatings for paper
- top coats for wood
- overprint varnishes
1,500
at 60℃
6 max. 1.18 850 2 100 5 max. TDS
MSDS
SE 1605 both acrylate and epoxy functionalities
- good adhesion on metal and non-porous substrate
- improved flexibility over other epoxy acrylates
- good cure response
- good solvent resistance
- high gloss
- substrates : metal
- coatings and inks for metal substrates including aluminum
- thermal post-curing will enhance coating properties
- 2-component curing systems
1,000
at 60℃
5 max. 1.17 450 1 100 1 max. TDS
MSDS
SE 1636 high functionality novolac epoxy acrylate with TMPTA
- high molecular weight
- excellent heat & heat resistance
- good adhesion on metal
- low shrinkage
- good hardness
- substrates : metal particularly copper
- UV solder resist for PCB
- adhesion to metalized substrate
- heat resistance application
- solder resist and off-contact
25,000
at 25℃
5 max. 1.16 1,000 3.5 65 5 max. TMPTA
35
TDS
MSDS
SE 1656 high functionality novolac epoxy acrylate with TMPTA
- good heat resistances
- good chemical resistances
- good adhesion on metal
- high molecular weight
- fast curing
- good hardness
- substrates : metal
- marking ink
- heat resistance application
- solder resist and off-contact
45,000
at 25℃
7 max. 1.15 1,000 3.2 50 5 max. TMPTA
50
TDS
MSDS
SE 1700 bisphenol A epoxy diacrylate
- fast curing
- good hardness
- high gloss
- good chemical resistances
- low odor
- substrates : paper, wood, plastic
- lithographic and screen inks and coatings
- fast cure coatings
- overprint varnishes
- wood fillers & top coats
- laminating adhesives
3,500
at 60℃
6 max. 1.18 525 2 100 2 max. TDS
MSDS
SE 1701 modified bisphenol A epoxy diacrylate
- excellent solvent resistance
- good abrasion resistance
- good flexibility
- good adhesion
- high gloss
- substrates : paper, wood, chip board, plastics
- lithographic and screen inks
- clear coatings for paper
- overprint varnishes
7,500
at 60℃
6 max. 1.20 1,000 2 100 5 max. TDS
MSDS
SE 1702 fatty acid modified bisphenol A epoxy diacrylate
- excellent flow and leveling
- good pigment wetting
- good solvent resistances
- high gloss
- good water resistances
- substrates : paper, wood, chip board, plastics
- lithographic and screen inks
- clear coatings for paper
- overprint varnishes
5,000
at 60℃
6 max. 1.14 500 2 100 5 max. TDS
MSDS
SE 1703 amine modified bisphenol A epoxy diacrylate
- fast cure response
- good flexibility
- high gloss
- good solvent resistances
- good adhesion to plastic
- substrates : paper, wood, chip board, plastics
- lithographic and screen inks
- top coats for wood
- clear coatings for paper
- overprint varnishes
3,250
at 60℃
6 max. 1.18 850 2 100 5 max. TDS
MSDS




 

SOLTECH LTD. (Head office) : #368-2, SANMAK-DONG, YANGSAN, KYOUNGNAM, 626-120, KOREA
PHONE : 82-(0)55-387-6468 / FAX : 82-(0)55-387-6470 / E-mail : info@uvpia.com

Copyright (C) 2010 by SOLTECH LTD. All rights reserved.